输送带破损后如何修复 How to repair the conveyor belt when it is damaged 1、输送带在运行中存在的磨损形式 1. Wear form of conveyor belt in operation 输送带更换的主要原因是磨损，磨损一般分为以下3种形式： The main reason for the replacement of the conveyor belt is wear, and the wear is generally divided into the following three forms: 1)输送带的硫化接头处磨损通常是由于输送带自身材料要比硫化接头处胶层的耐磨度高或热硫化质量问题，造成硫化接头胶层局部磨损，露出钢丝芯或尼龙芯，对输送带之间的硫化接头强度构成严重威胁。 1) wear is usually due to the conveyor belt conveyor belt sulfide tapping their material than the vulcanized rubber joint wear-resisting degree is high or hot vulcanization quality problem, cause partial wear rubber vulcanization joint, or steel wire core, the godson, strength of conveyor belt between the vulcanization joint pose a serious threat. 2)输送带在裙板部位磨损 2) wear the conveyor belt in the apron area 由于输送带导料装置的裙板调整不当或者导料裙板设计不良，会导致裙板在运行中磨损输送带，造成输送带两侧上胶层磨损严重，整条胶带纵向运行方向露出钢绳芯或尼龙芯，一旦钢绳芯翘起，极易缠绕到托辊上，造成钢丝带脱丝或胶带的撕裂。 Due to improper apron conveyor belt feed device adjustment or feed apron poorly designed, can lead to wear in the operation of the apron in conveyor belt, causing a rubber conveyor belt on both sides of the serious wear and tear, and the whole belt longitudinal direction with steel rope or the godson, once steel wire core, cock is winding to the roller, steel wire with wire or tape tearing off. 3)输送带中间部位磨损这是由落料冲击造成的，由于漏斗的落料点相对固定，因此输送带承受冲击的部位磨损加剧，造成输送带沿运行方向局部磨损严重，也会导致露出的钢绳芯脱丝或输送带撕裂。对于尼龙胶带则造成中间部位强度下降，由于承载托辊存在3。～4。的前倾角，所以在承载托辊趋中力的作用下，胶带运行中会出现“叠带”的危险现象。 3) conveyor belt middle wear this is caused by dropping impact, as a result of the funnel blanking point relatively fixed, so the conveyor belt parts under impact wear, cause local wear in the conveyor belt along the direction of, can also lead to reveal the steel wire rope off or belt tearing. In the case of nylon tape, the strength of the middle part is reduced, because the bearing roller is 3. ~ 4. The front rake Angle, so in carrying the supporting roller toward the force of the action, the belt will appear the dangerous phenomenon of "overlapping belt".