| 输送带冷硫化修补 Cold vulcanizing repair of conveyor belt 1.将输送带破损部位用角磨机配合钨钢打磨碟进行打磨。 1. grinding the damaged parts of the conveyor belt with the angle grinder and tungsten steel grinding disc. 2.根据输送带破损部位的大小选择相应的带半硫化层的输送带修补片或修补条(修补条或修补片至少大出破损部位15~20mm)茵美特建议使用带半硫化层修补条、修补片，不带半硫化层的材料建议将粘接面进行深层次打磨。 2. According to the size of the damaged part of the conveyor belt, choose the corresponding belt patch or patch with semi-vulcanized layer (patch or patch at least 15-20 mm larger than the damaged part). Imet suggests using semi-vulcanized layer patch or patch, and the material without semi-vulcanized layer suggests deep polishing of the bonding surface. 3.将输送带破损部位和输送带修补条半硫化面进行涂刷皮带胶，晾置一会，然后进行第二遍涂刷(晾置至不粘手为止，常温情况下一般在五分钟)。 3. Brush belt glue on the damaged part of conveyor belt and semi-vulcanized surface of repairing strip of conveyor belt for a while, then brush it for a second time (air until no sticking hands, usually for five minutes at room temperature). 4.将修补条拉直贴在输送带打磨面上，用橡胶锤或者压实滚轮进行敲打压实，赶出空气。 4. Straighten the repair strip on the grinding surface of the conveyor belt, knock and compact with a rubber hammer or compacting roller, and drive out the air. 温馨提示：若环境温度过低建议使用碘钨灯或热风枪加热0.5-1小时，时间若允许适当延长加热时间，将有利于粘接面强度的提高。 Warm reminder: If the ambient temperature is too low, it is recommended to use iodine tungsten lamp or hot air gun to heat for 0.5-1 hours. If the heating time is allowed to prolong properly, it will be beneficial to improve the strength of the bonding surface. |
| 上一页 输送带的用途和材质知识点 |
| 下一页 裙边输送带的保养与说明 |
Copyright © 技术支持：遨游网络